薛勇,郑杰,闫钊鸣,徐健,张治民,李旭斌,杨勇彪,王强.差速循环扩挤制备的AZ31镁合金的组织和力学性能[J].稀有金属材料与工程,0,():-.[xueyong,zhengjie,yanzhaoming,xujian,zhangzhimin,lixubin,yangyongbiao,wangqiang.Microstructure and mechanical properties of AZ31 magnesium alloy prepared by cyclic expansion-extrusion with an asymmetrical extrusion cavity (CEE-AEC)[J].Rare Metal Materials and Engineering,0,():-].
本文是作者原稿,未经编辑加工,请引用时标明待出版或者标注网页。最终应以正式出版稿为准。
差速循环扩挤制备的AZ31镁合金的组织和力学性能
投稿时间:2020-05-11  修订日期:2020-06-16
中文关键词:  镁合金  循环扩挤  微观结构  机械性能
基金项目:National Natural Science Foundation of China (Grant No. 51675492); Natural Science Foundation of Shanxi Province (Grant No. 201801D121106)
中文摘要:
      对AZ31镁合金进行了差速循环扩挤(CEE-AEC),研究了变形道次对晶粒细化、织构演变和力学性能的影响。结果表明,在差速循环扩挤过程中,发生了连续动态再结晶(CDRX)和非连续动态再结晶(DDRX),平均晶粒尺寸从344μm减小到11.7μm。随着加工道次的增加,(0001)基面织构强度逐渐增加。差速循环扩挤模具中不对称型腔的存在极大地引起了基面织构的偏转。此外,合金的机械性能得到改善,并且抗拉屈服强度(TYS),极限抗拉强度(UTS)和断裂伸长率(EF)分别为109 MPa,211 MPa和30.8%。
Microstructure and mechanical properties of AZ31 magnesium alloy prepared by cyclic expansion-extrusion with an asymmetrical extrusion cavity (CEE-AEC)
英文关键词:Magnesium alloy  cyclic expansion-extrusion  microstructure  mechanical property
英文摘要:
      Cyclic expansion-extrusion with an asymmetrical extrusion cavity (CEE-AEC) was performed on AZ31 magnesium alloy, and the effects of deformation passes on grain refinement, texture evolution, and mechanical properties were studied. The results show that during the CEE-AEC process, continuous dynamic recrystallization (CDRX) and discontinuous dynamic recrystallization (DDRX) occurred, and the average grain size is reduced from 344 μm to 11.7 μm. The (0001) basal texture intensity gradually increases with the increase of processing passes. The existence of asymmetric cavities in CEE-AEC dies drastically caused a deflection of the basal texture. In addition, the mechanical properties of the alloy are improved, and the tensile yield strength (TYS), ultimate tensile strength (UTS), and elongation to fail (EF) are 109 MPa, 211 MPa, and 30.8%, respectively.
作者单位
薛勇 中北大学材料科学与工程学院 
郑杰 中北大学材料科学与工程学院 
闫钊鸣 中北大学材料科学与工程学院 
徐健 中北大学材料科学与工程学院 
张治民 中北大学材料科学与工程学院 
李旭斌 中北大学材料科学与工程学院 
杨勇彪 中北大学材料科学与工程学院 
王强 中北大学材料科学与工程学院 
摘要点击次数: 24
全文下载次数: 0
  查看/发表评论  
关闭